Fraises à queue courtes, 45°, type HR, Weldon, revêtement AlCrN
|
D
h 10 |
d
h 6 | l1 | l2 | l3 | Dn | Z | Code article | En stock |
|---|---|---|---|---|---|---|---|---|
| 4 | 6 | 54 | 8 | 13 | 3,8 | 3 | S118612N.040 AlCrN | Oui |
| 5 | 6 | 54 | 9 | 16 | 4,8 | 4 | S118612N.050 AlCrN | Oui |
| 6 | 6 | 54 | 10 | 17 | 5,7 | 4 | S118612N.060 AlCrN | Oui |
| 8 | 8 | 58 | 12 | 22 | 7,6 | 4 | S118612N.080 AlCrN | Oui |
| 10 | 10 | 66 | 14 | 26 | 9,5 | 4 | S118612N.100 AlCrN | Oui |
| 12 | 12 | 73 | 16 | 28 | 11,5 | 4 | S118612N.120 AlCrN | Oui |
| 14 | 14 | 75 | 18 | 30 | 13,5 | 4 | S118612N.140 AlCrN | Non |
| 16 | 16 | 82 | 22 | 34 | 15,5 | 4 | S118612N.160 AlCrN | Oui |
| 16 | 16 | 82 | 22 | 34 | 15,5 | 5 | S118612N.160Z5 AlCrN | Oui |
| 18 | 18 | 84 | 24 | 36 | 17,5 | 5 | S118612N.180 AlCrN | Non |
| 20 | 20 | 92 | 26 | 42 | 19,5 | 5 | S118612N.200 AlCrN | Oui |
| 20 | 20 | 92 | 26 | 42 | 19,5 | 6 | S118612N.200Z6 AlCrN | Non |
Conditions de coupe
Matériaux |
Dureté |
Ap |
Ae |
Vc |
fz(mm/z) Ø 4 |
Ø 6 |
Ø 8 |
Ø 10 |
Ø 12 |
Ø 16 |
Ø 18 |
Ø 20 |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| P.1 | Acier de coupe, acier de construction | ≤ 600 N/mm² | 1xD | 0,4xD | 210 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| P.3 | Acier à outils faiblement allié | ≤ 1100 N/mm² | 1xD | 0,4xD | 175 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| P.5 | Acier à outils fortement allié | ≤ 1100 N/mm² | 1xD | 0,4xD | 120 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| M.1 | Acier inoxydable | ≤ 750 N/mm² | 1xD | 0,4xD | 110 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| M.2 | Acier inoxydable | 750 - 850 N/mm² | 1xD | 0,4xD | 90 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| K.1 | Fonte (≤ 240 HB) | ≤ 820 N/mm² | 1xD | 0,4xD | 150 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| K.2 | Fonte (> 240 HB) | > 800 N/mm² | 1xD | 0,4xD | 110 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| S.1 | Alliage Cr-Ni | ≤ 1500 N/mm² | 1xD | 0,4xD | 50 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| H.1 | Acier trempé (< 54 HRC) | < 1920 N/mm² | 1xD | 0,4xD | 120 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
| H.2 | Acier trempé (54 - 60 HRC) | 1920 - 2210 N/mm² | 1xD | 0,4xD | 100 | 0.02 | 0.03 | 0.04 | 0.055 | 0.065 | 0.085 | 0.1 | 0.11 |
Attributs du produit
Queue weldon - DIN 6535 HB.
Angle d'Hélice = 45°.
Angle de Pointe = 6°.
Élaboration de la tête
Les matériaux en carbure se caractérisent par une résistance élevée à la compression, une dureté élevée et donc une grande résistance à l'usure, mais aussi une résistance à la flexion et une ténacité limitées.
Pour opération d'ébauche des matériaux d´une résistance moyenne et plus élevée (jusqu'à 1200 MPa), la rugosité de surface Ra 6,3 et grossière.
Directions possibles de mouvement
Refroidissement par air
Revêtement avec une haute résistance abrasive, avec stabilité et la ténacité à des températures élevées.